• Boiler & Pressure Vessel Steel Plate A516M
  • Boiler & Pressure Vessel Steel Plate A573M
  • Boiler & Pressure Vessel Steel Plate EN10028-3
  • Boiler & Pressure Vessel Steel Plate GB/T713-97
  • Boiler & Pressure Vessel Steel Plate DIN17155

Boiler & Pressure Vessel Steel Plate

  • Thickness: 1.2mm-400mm
  • Width: 50mm-4020mm
  • Length: 50mm-18000mm
  • Steel Grade: A515M, A516M, A573M, EN10028-3, GB/T713-97,DIN17155
■ Full Data
♦ Specification Range & Status on Delivery

1.Specification Range

Plate
Thickness:6mm-400mm
Width:50mm-4020mm
Length:50mm-18000mm

Coil
Thickness:1.2mm-19mm
Width:50mm-2000mm
Length:Can't less than 50mm

2. MOQ for each order
25 Ton Status on Delivery: According to the performance and the requirements from clients, the status on delivery of steel plate can be hot rolled , controlled rolling, normalizing, annealed tempering, normalizing + tempering, hardening + tempering , etc.

3. flaw detection & Through-Thickness Property
We are capable of manufacturing the steel plate with additional flaw detection and Z15-Z35 tear resistance ( Through-Thickness Property ), also can supply you with Z-Direction Steel Plate according to ASTM、A770 standard.

♦ Application of Boiler & Pressure Vessel Steel Plate
Widely used in petroleum, chemical industry, power plants, boilers and other fields,such as to produce reactors, heat exchangers, separators, spherical tank, oil tank, LPG tanks, nuclear reactor pressure shell,boiler drum, liquefied petroleum gas cylinders, hydropower high-pressure pipes, Turbine vortex shells and other equipment and components, etc.

Steel Grade
Executive Standard
20g,16Mng,15CrMog 12CrlMoVg,19Mng 22Mng,13MnNiCrMoNbg
GB713-97
20R,16MnR,15MnVR 15CrMoR,13MnNiMoNbR 15MnNbR,15MnVNR
GB6654-96
16MnDR,09MnNiDR,15MnNiDR
GB3531
12Cr2Mo1R,14Cr1MoR 07MnCrMoVR,07MnNiCrMoVDR
GB150
SB410,SB450,SB480
JIS G 3103
SPV235,SPV315,SPV355 SPV410,SPV450,SPV490
JIS G 3115
SGV410,SGV450,SGV480
JIS G 3118
SBV1A,SBV1B,SBV2,SBV3
JIS G 3119
SEV245,SEV295,SEV345
JIS G 3124
HI,HII,10CrMo910,15Mo3 13CrMo44,19Mn6
DIN17155
BHW35
Thyssen
13MnNiMo54
Dillingen
1Cr0.5Mo,2.25Cr1Mo 1.25Cr0.5Mo
special purpose & condition
(S)A299M
(S)A515M(Gr.60,65,70)
(S)A516M(Gr.55,60,65,70)
(S)A204M(Gr.A,B,C)
(S)A387M(Gr.11,12,22)
(S)A537M(CL.1,CL.2)
(S)A662M(Gr.A,B,C)
(S)A302M(Gr.A,B,C,D)
(S)A737M(Gr.B,C)
(S)A738M(Gr.A,B,C)
(S)A533M(I,II)
ASTM、ASME
P235GH,P265GH,P295GH
P355GH,16Mo3,13CrMo4-5
10CrMo9-10,11CrMo9-10
EN10028-2
A42,A52,A48
NF A36-205
20MnHR,20HR,16MnHR
special purpose & condition
161G430
BS1501
■ Features
Typical material of Boiler steel plate

1 Chemical compostion of Boiler & Pressure Vessel Steel Plate

Brand C≤ Mn≤ Si≤ P≤ S≤ Alt≥
Q245R 0.20 0.5-1 0.3-5 0.025 0.015 0.020

2 Mechanical property of Boiler & Pressure Vessel Steel Plate

Brand Yield point σs,MPa Tensile strength σb MPa Elongation δ5 % Longitudinal impact strength,AkV,J(℃) 180° Bending test d=Diameter of apex a= Specimen thickness
≤16 >16-36 >36-60 >60-100 20 0 -20 -40  
Not less than Not less than ≥35
Q245R 245 235 225 205 390-520 25   31     1.5a 2a

Typical material of Pressure vessel steel plate

1 Chemical compostion of 
Boiler & Pressure Vessel Steel Plate

Brand C≤ Mn≤ Si≤ P≤ S≤ Alt≥
Q345R 0.20 1.2-1.6 0.5-5 0.025 0.015 0.020

2. Mechanical property of Boiler & Pressure Vessel Steel Plate

Brand Yield point σs,MPa Tensile strength σb MPa Elongation δ5 % Longitudinal impact strength,AkV,J(℃) 180° Bending test d=Diameter of apex a= Specimen thickness
≤16 >16-36 >36-60 >60-100 20 0 -20 -40
Not less than Not less than ≥35
Q345R 345 325 315 305 490-640 21   34     2a 3a

ASME SA516 Gr. 60 / ASTM A516 Gr. 60 - the specification
A516 / SA516 is a remarkably straightforward standard in its basic form with just five key chemical elements specified along with three mechanical properties.

Chemical Requirements

Element Thickness Composition (%) Note
Carbon (max) 12.5 mm and under 0.21 A, B, C
  over 12.5 to 50 mm 0.23 A, B, C
  over 50 to 100 mm 0.25 A, B, C
  over 100 mm 0.27 A, B, C
Manganese 12.5 mm and under 0.60 - 0.90 A, C, D
  12.5 mm and under 0.55 - 0.98 B, C, D
  over 12.5 mm 0.85 - 1.20 A, C
  over 12.5 mm 0.79 - 1.30 B, C
Phosphorus (max)   0.025 A, B
Sulphur (max)   0.025 A, B
Silicon   0.15 - 0.40 A
    0.13 - 0.45 B
Notes: A - heat analysis, B - product analysis, C - For each reduction of 0.01% below the specified maximum for Carbon, an increase of 0.06% above the specified maximum for Managanese is permitted, up to a maximum of 1.50% by heat analysis and 1.60% by product analysis, D - Plates 12.5 mm and under may have 0.85 - 1.20% Manganese on heat analysis and 0.79 - 1.30% on product analysis.

Tensile Requirements

Mechanical Property Value
Tensile Strength, MPa (ksi) 415 - 550 (60 - 80)
Yield Strength, min MPa (ksi) 220 (32)
Elongation min, % 200 mm (8 in) 21
Elongation min, % 50 mm (2 in) 25

ASME SA516 Gr. 65 / ASTM A516 Gr. 65 - the specification The chemical and mechanical requirements of A516 / SA516 are very simple and these are listed below. Further complexity comes from additional supplementary requirements and end-user produced variations: needless to say, Brown McFarlane is able to supply Grade 65 plates that will meet the most stringent specifications.

Chemical Requirements

Element Thickness Composition (%) Note
Carbon (max) 12.5 mm and under 0.24 A, B, C
  over 12.5 to 50 mm 0.26 A, B, C
  over 50 to 100 mm 0.28 A, B, C
  over 100 mm 0.29 A, B, C
Manganese   0.85 - 1.20 A, C
    0.79 - 1.30 B, C
Phosphorus (max)   0.025 A, B
Sulphur (max)   0.025 A, B
Silicon   0.15 - 0.40 A
    0.13 - 0.45 B
Notes: A - heat analysis, B - product analysis, C - For each reduction of 0.01% below the specified maximum for Carbon, an increase of 0.06% above the specified maximum for Managanese is permitted, up to a maximum of 1.50% by heat analysis and 1.60% by product analysis.

Tensile Requirements

Mechanical Property Value
Tensile Strength, MPa (ksi) 450 - 585 (65 - 85)
Yield Strength, min MPa (ksi) 240 (35)
Elongation min, % 200 mm (8 in) 19
Elongation min, % 50 mm (2 in) 23
ASME SA516 Gr. 70 / ASTM A516 Gr. 70 - the specification

Despite its wide use and application, A516 / SA516 is a remarkably straightforward standard in its basic form with just five key chemical elements specified along with three mechanical properties. It does not even need to be heat treated in any way.

Chemical Requirements

Element Thickness Composition (%) Note
Carbon (max) 12.5 mm and under 0.27 A, B, C
  over 12.5 to 50 mm 0.28 A, B, C
  over 50 to 100 mm 0.30 A, B, C
  over 100 mm 0.31 A, B, C
Manganese   0.85 - 1.20 A, C
    0.79 - 1.30 B, C
Phosphorus (max)   0.025 A, B
Sulphur (max)   0.025 A, B
Silicon   0.15 - 0.40 A
    0.13 - 0.45 B
Notes: A - heat analysis, B - product analysis, C - For each reduction of 0.01% below the specified maximum for Carbon, an increase of 0.06% above the specified maximum for Managanese is permitted, up to a maximum of 1.50% by heat analysis and 1.60% by product analysis.

Tensile Requirements

Mechanical Property Value
Tensile Strength, MPa (ksi) 485 - 620 (70 - 90)
Yield Strength, min MPa (ksi) 260 (38)
Elongation min, % 200 mm (8 in) 17
Elongation min, % 50 mm (2 in) 21

ASME SA537 Class 1 / ASTM A537 Class 1 - the specification

Chemical Requirements

Element Thickness Composition (%) Note
Carbon (max)   0.24 A, B
Manganese 40 mm and under 0.70 - 1.35 A, C
  40 mm and under 0.64 - 1.46 B, C
  Over 40 mm 1.00 - 1.60 A, C
  Over 40 mm 0.92 - 1.72 B, C
Phosphorus (max)   0.035 A, B
Sulphur (max)   0.035 A, B
Silicon   0.15 - 0.50 A
    0.13 - 0.55 B
Copper (max)   0.35 A
    0.38 B
Nickel (max)   0.25 A, C
    0.28 B, C
Chromium (max)   0.25 A
    0.29 B
Molybdenum (max)   0.08 A
    0.09 B
Notes: A - heat analysis, B - product analysis, C - Manganese may exceed 1.35% on heat analysis, up to a maximum of 1.60%, and Nickel may exceed 0.25% on heat analysis, up to a maximum of 0.50%, provided the heat analysis carbon equivalent (long formula) does not exceed 0.57%. When this option is exercised, the Manganese and Nickel contents on product analysis shall not exceed the heat analysis content by more than 0.12% and 0.03% respectively.

Tensile Requirements

Mechanical Property Value
Tensile Strength, MPa (ksi) 485 - 620 (70 - 90)
Yield Strength, min MPa (ksi) 345 (50)
Elongation min, % 200 mm (8 in) 18
Elongation min, % 50 mm (2 in) 22
Note: The above values are applicable to plates 65 mm and under. Values for thicker plates are available from our sales and technical teams.